Exfoliated nanocomposites and articles containing same

ABSTRACT

A polymeric nanocomposite comprises a non-polar hyperbranched polystyrene resin. An exfoliated or intercalated onium functionalized clay is dispersed within the resin. Such nanocomposites are more compatible with non-polar polymer matrices used in various articles of manufacture.

CROSS-REFERENCE TO RELATED APPLICATIONS

This is a Divisional of application U.S. Ser. No. 12/240,073 filed Sep.29, 2008, entitled “Exfoliated Nanocomposites And Articles ContainingSame”, now allowed.

FIELD OF THE INVENTION

This invention relates to exfoliated or intercalated polystyrene-claynanocomposite compositions, and to articles in which these compositionsare incorporated.

BACKGROUND OF THE INVENTION

There have been extensive efforts directed towards the preparation ofvarious polymer-clay composite materials since the discovery ofexfoliated nylon/clay nanocomposites by Usuki et al. (J. Mater. Res.1993, 8, 1174). Such materials are expected to have new and improvedmechanical, thermal, and barrier properties compared to those of thepolymers alone.

Incorporation of a few percent of clay has been found to greatlyincrease a polymer's modulus, strength, gas barrier properties, and heatdistortion temperature. The presence of clay is also reported to impartfire retardant properties. Without wishing to be bound by theory, theimprovement in thermal stability is believed to be attributed totortuous diffusion of the volatile thermal and thermo-oxidativedecomposition products in the presence of dispersed silicate layers. Theslower diffusion of decomposed volatiles along with structuralreinforcement provided by the char formed with collapsing silicatelayers during combustion contributes to decreased flammability ofexfoliated nanocomposite as demonstrated by cone calorimetry. See forexample, J. Zhu and C. A. Wilkie Polym. Int. 2000, 49, 1158; and J. W.Gilman Appl. Clay Sci. 1999, 15, 31.

The most common morphology for miscible polymer-clay dispersions isknown as intercalation. In this case, the host polymer penetrates thespace between the clay platelets, but separating them only slightly andmaintaining the parallel, regular structure of the platelets.Intercalated polymer-clay nanocomposites are often observed to havemeasurable improvements in physical properties, but typically less sothan if the corresponding nanocomposites were in the morphology known asexfoliation. Although exfoliation is much more desirable, it is lesscommon and more difficult to obtain. In this morphology, the clayplatelets are thoroughly separated from each other by the host polymer,so that their original crystallographic register is lost. Particularlyfor nonpolar polymer hosts, the fully exfoliated polymer-claynanocomposites are notoriously difficult to obtain.

Non-polar polymers, including polystyrene and polyethylene, represent agroup of commercially important thermoplastics. Polystyrene and linearlow density polyethylene (LLDPE) homopolymers form intercalatemorphologies when melt blended with organically modified clays known asorganoclays. See, for example, R. A. Vaia and E. P. GiannelisMacromolecules 1997, 30, 8000, and also K. H. Wang et al. Polymer, 2001,42, 9819.

Although exfoliation of clay in these non-polar polymers is moredesirable, achieving this state of morphology is particularlychallenging because the polymers are not strongly attracted to the claysurfaces. One approach to achieve this goal is in-situ polymerization ofnon-polar monomers in the presence of organoclay bearing eitherpolymerizable functional groups or initiators. See, for example, X. Fuand S. Qutubuddin Polymer 2001, 42, 807; J. Zhu et al, Chem. Mater.2001, 13, 3774; and M. W. Weimer et al. J. Am. Chem. Soc. 1999, 121,1615.

Another method to achieve exfoliation of such non-polar polymers is toincorporate polar units in the backbone of non-polar guest polymers andsubsequently melt blend them with a host organoclay. See, for example,N. Hasegawa et al. J. Appl. Polym. Sci. 1999, 74, 3359; and C. I. Parket al. Polymer 2001, 42, 7465. The latter strategy is industrially morefeasible, but increasing the fraction of polar units in non-polarpolymers may result in undesirable morphological changes, e.g., phaseseparation. Thus, complete exfoliation of organoclay in non-polarhomopolymer has not been commercially or economically practicable on acomparable scale.

U.S. Pat. No. 7,166,657 (Rao et al.) describes the use of highlybranched polar polymers to splay various clays to form nanocompositesfor various uses.

U.S. Pat. No. 6,686,407 (Robello, et al.) describes the use ofstar-branched polystyrene to achieve exfoliation of organoclays. Atheoretical treatment of this approach is given by Singh and Balazs(Polym. Int. 2000, 49, 469). Exfoliated nanocomposites were achieved,but such star-branched polymers are laborious and expensive tosynthesize and a more practical technique is highly desirable.

PROBLEM TO BE SOLVED

There is a need to provide nanocomposites using non-polar polymers withclays using less expensive reactants and methods of preparation. Suchnanocomposites would be more compatible with non-polar polymer matricesused in various articles of manufacture and exhibit improved physicalstrength as well as other properties.

SUMMARY OF THE INVENTION

The present invention is directed to a polymeric nanocompositecomprising a non-polar hyperbranched polystyrene resin and havingdispersed therein an exfoliated or intercalated onium functionalizedclay.

This invention also provides an article comprising a matrix and apolymeric nanocomposite comprising a non-polar hyperbranched polystyreneresin and having dispersed therein an exfoliated or intercalated oniumfunctionalized clay.

The present invention polymeric nanocomposites with improved strengthand compatibility with non-polar materials into which they can be mixedfor various articles of manufacture.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a black and white image of the coating provided in ComparativeExample 1 below.

DETAILED DESCRIPTION OF THE INVENTION

Unless otherwise indicated, whenever used herein, the terms set forthshall herein have the following meaning:

“Nanocomposite” means a composite material wherein at least onecomponent comprises an inorganic phase, such as a smectite clay, with atleast one dimension in the 0.1 to 100 nm range.

“Plates” means particles with two comparable dimensions significantlygreater than the third dimension, for example, length and width of theparticle being of comparable size but orders of magnitude greater thanthe thickness of the particle.

“Layered material” means an inorganic material such as a smectite claythat is in the form of a plurality of adjacent bound layers.

“Platelets” means individual layers of the layered material.

“Intercalation” means the insertion of one or more foreign molecules orparts of foreign molecules between platelets of the layered material,usually detected by X-ray diffraction technique, as illustrated in U.S.Pat. No. 5,891,611 (Majumdar et al., line 10, Col. 5-line 23, Col. 7).

“Intercalant” refers to the aforesaid foreign molecule inserted betweenplatelets of the aforesaid layered material.

“Exfoliation” or “delamination” means the separation of individualplatelets in to a disordered structure without any stacking order. Theterm “substantially exfoliated” means that at least 80 percent of theoriginal background-subtracted X-ray diffraction peak intensity (height)due to the (001) basal plane has been lost, as shown by a standardmeasurement. The term “(001) basal plane” shall refer to the spacingbetween a layer of silicate atoms in one plane to the correspondinglayer of silicate atoms in another plane, including any material presentbetween layers. This can also be referred to as basal plane spacing ord(001).

“Intercalated” refers to a layered material that has at least partiallyundergone intercalation. This can also include a material that hasundergone both partial intercalation and partial exfoliation.

“Organoclay” means a clay material that has been modified by organicmolecules.

“Swellable” refers to a layered material capable of showing an increaseor expansion in spacing between layers resulting from insertion ofspecies into the layered material.

Clays in a polystyrene-clay nanocomposites of the present invention canbe ideally thought to exist in one of two structures: (1) intercalatedclay wherein the clay lattice has been expanded to a thermodynamicallydefined equilibrium spacing due to the insertion of individualpolystyrene chains, yet maintaining a long range order in the lattice,and (2) substantially or entirely exfoliated clay wherein singular clayplatelets are randomly suspended in the polystyrene, resulting fromextensive penetration of the polystyrene into the clay lattice and itssubsequent delamination. As indicated above, the greatest propertyenhancements of polystyrene-clay nanocomposites are expected with thestructure (2) mentioned above.

The clay material suitable for use in this invention can comprise anyinorganic phase comprising layered materials in plates or other shapeswith a significantly high aspect ratio. The clay materials suitable forthis invention include phyllosilicates, for example, montmorillonite(such as particularly sodium montmorillonite, magnesium montmorillonite,and calcium montmorillonite), nontronite, beidellite, volkonskoite,hectorite, saponite, sauconite, sobockite, stevensite, svinfordite,vermiculite, magadiite, kenyaite, talc, mica, kaolinite, and mixturesthereof. Other useful layered materials include illite, mixed layeredillite/smectite minerals, such as ledikite and admixtures of illiteswith the clay minerals named above. Other useful layered materials, arethe layered double hydroxides or hydrotalcites, such asMg₆Al_(3.4)(OH)_(18.8)(CO₃)_(1.7)H₂O, which have positively chargedlayers and exchangeable anions in the interlayer spaces. Other layeredmaterials having little or no charge on the layers may be usefulprovided they can be intercalated with swelling agents, which expandtheir interlayer spacing. Such materials include chlorides such asFeCl₃, FeOCl, chalcogenides, such as TiS₂, MoS₂, and MoS₃, cyanides suchas Ni(CN)₂ and oxides such as H₂Si₂O₅, V₆O₁₃, HTiNbO₅,Cr_(0.5)V_(0.5)S₂, V₂O₅, Ag doped V₂O₅, W_(0.2)V_(2.8)O7, Cr₃O₈,MoO₃(OH)₂, VOPO₄-2H₂O, CaPO₄CH₃—H₂O, MnHAsO₄—H₂O, and Ag₆Mo₁₀O₃₃. Manyuseful clays are swellable. These swellable clays includephyllosilicates of the 2:1 type, as defined in clay literature (vide,for example, H. van Olphen An Introduction to Clay Colloid Chemistry,John Wiley & Sons Publishers, 1977, hereby incorporated by reference).Typical phyllosilicates with ion exchange capacity of 50 to 300milliequivalents per 100 grams are preferred. Preferred clays for thepresent invention include smectite clay such as montmorillonite,nontronite, beidellite, volkonskoite, hectorite, saponite, sauconite,sobockite, stevensite, svinfordite, halloysite, magadiite, kenyaite andvermiculite as well as layered double hydroxides or hydrotalcites.Montmorillonite, hectorite and hydrotalcites are useful because of theireffectiveness in the present invention and/or the commercialavailability of these materials. In some embodiments, the clay is amontmorillonite, hectorite, saponite, nontronite, beidellite,volkonskoite, sauconite, magadiite, medmontite, kenyaite, orvermiculite.

The aforementioned clays can be natural or synthetic, for examplesynthetic smectite clay. This distinction can influence the particlesize and/or the level of associated impurities. Typically, syntheticclays are relatively smaller than natural clays in lateral dimension,and therefore possess smaller aspect ratio. However, synthetic clays arepurer and are of narrower size distribution, compared to natural clays,and may not require any further purification or separation. For thisinvention, the clay particles generally should have (on average) alateral dimension of from about 0.01 μm to about 5 μm, and typicallyfrom about 0.05 μm to about 2 μm, and or from about 0.1 μm to about 1μm. The thickness or the vertical dimension of the clay particles canvary (on average) of from about 0.5 nm to about 10 nm, and typicallyfrom about 1 nm to about 5 nm. The aspect ratio, which is the ratio ofthe largest and smallest dimensions of the clay particles can be greaterthan 10:1 and typically greater than 100:1. The aforementioned limitsregarding the size and shape of the particles are designed to ensureadequate improvements in some properties of the nanocomposites withoutdeleteriously affecting others. For example, a large lateral dimensionmay result in an increase in the aspect ratio, a desirable criterion forimprovement in mechanical and barrier properties. However, very largeparticles can cause optical defects, such as haze, and can be abrasiveto processing, conveyance and finishing equipment as well as the imaginglayers.

The clay used in this invention is an organoclay that has been producedby interacting or pretreating the unfunctionalized clay with a suitableonium salt intercalant. Useful onium species include ammonium (primary,secondary, tertiary, and quaternary), phosphonium, or sulfoniumderivatives of aliphatic, aromatic or arylaliphatic amines, phosphinesand sulfides. Typically, onium ions can cause intercalation in thelayers through ion exchange with the metal cations of the smectite clay.

The organoclay useful in the present invention is generally present inthe nanocomposite in an amount of at least 1 and up to 50 weight %, orfrom about 20 to about 30 weight %.

The matrix polymer includes one or more non-polar hyperbranchedpolystyrenes that can have a variety of non-polar substituents on thestyrene group within the polymer chain(s). By hyperbranched, we mean apolydispersed dendritic macromolecule that is imperfectly branched inwhich the branches do not emanate from a central core. Suchhyperbranched polymers can be obtained from a number of commercialsources or prepared using known reactants and reaction conditions. Forexample, the hyperbranched polystyrene resin can have from 95% to 100%recurring units that are derived unsubstituted styrene.

The molecular weight of the hyperbranched polystyrene is at least 2,000and can be as high as 1,000,000.

The hyperbranched polystyrene is present in the nanocomposite in anamount of at least 2 and up to 95 weight %, or from about 8 to about 20weight %. The weight ratio of the onium functionalized clay to thehyperbranched polystyrene resin is generally from about 1:1 to about0.1:1 or from about 0.3:1 to about 0.2:1. The optimum ratio can bereadily determined by routine experimentation for a given use.

The polymeric nanocomposite of this invention can be formed by meltblending the organoclay with the hyperbranched polystyrene resin at atemperature that is at or above the hyperbranched polystyrene meltingpoint, with or without shear. Alternatively, the organoclay andhyperbranched polystyrene can be mixed in a suitable solvent or mixtureof solvents.

The final mixture of the nanocomposite composition may include variousoptional components which are additives commonly employed with polymers.Such optional components may be added to the polymer melt or later andinclude nucleating agents, fillers, antioxidants, preservatives,plasticizers, impact modifiers, chain extenders, plasticizers,colorants, mold release lubricants, antistatic agents, pigments, fireretardants, and the like. These optional components and appropriateamounts are well known to those of skill in the art.

The nanocomposites of this invention exhibit useful properties. Thenanocomposite compositions according to the invention are thermoplasticmaterials from which molded articles of manufacture having valuableproperties can be produced by conventional shaping processes, such asmelt spinning, casting, vacuum molding, sheet molding, injection moldingand extruding. Examples of such molded articles are components fortechnical equipment, apparatus castings, household equipment, sportsequipment, bottles, containers, components for the electrical andelectronics industries, car components, circuits, fibers, foamedarticles such as cups, sheets, building insulation, etc., semi-finishedproducts which can be shaped by machining and the like. The use of thematerials for coating articles by means of powder coating processes isalso possible, as is their use as hot-melt adhesives. The moldingcompositions according to the invention are outstandingly suitable forspecific applications of all types since their spectrum of propertiescan be modified in the desired direction in manifold ways.

Such articles can include a suitable matrix such as a polymeric matrixinto which the polymeric nanocomposite is incorporated. The weight ratioof the matrix to the polymeric nanocomposite can be from about 10:1 toabout 100:1.

The molding compositions according to the invention are outstandinglysuitable for the production of sheets and panels having valuableproperties. Such sheets and panels may be shaped by conventionalprocesses such as vacuum processing, a molding processing, or by hotpressing to form useful objects. The sheets and panels according to theinvention are also suitable for co-extruding with other materials or ascoating materials for other materials comprising, for example, wood,glass, ceramic, metal or other plastics, and outstanding strengths canbe achieved using conventional adhesion promoters, for example, thosebased on vinyl resins. The sheets and panels can also be laminated withother plastic films and this is preferably obtained by co-extrusion, thesheets being bonded in the molten state. The surfaces of the sheets andpanels, including those in the embossed form, can be improved orfinished by conventional methods, for example by lacquering or by theapplication of protective films.

The compositions of this invention are useful for fabrication ofextruded films and film laminates, as for example, films for use in foodpackaging. Such films can be fabricated using conventional filmextrusion techniques. The films are preferably from about 10 to about100 microns, more preferably from about 20 to about 100 microns and mostpreferably from about 25 to about 75 microns in thickness. In the film,the major plane of the platelet fillers is substantially parallel to themajor plane of the film. The extent of parallelism of particles and filmcan be determined by X-ray diffraction analysis.

The following specific examples are presented to more particularlyillustrate the invention and are not to be construed as limitationsthereon.

Comparative Example 1

This specific example demonstrates the incompatibility of certainhyperbranched polymers with non-polar polymer matrices in contrast toU.S. Pat. No. 7,166,657 (Rao et al.). Into a glass vessel was charged1.21 grams of a linear, non-hyperbranched polystyrene (Aldrich, averagemolecular weight 45,000), and 0.30 grams of a 90:10 weight:weightHybrane P/S (hyperbranched polyester amide) Laponite RDS freeze driedpowder mixture (a non-functionalized clay with no onium surface groups).The combined polystyrene and Hybrane P/S: Laponite RDS freeze driedpowder mixtures are referred to as the “Comparative Composite.” Afterdry mixing the Comparative Composite powder, the vessel was then placedon a Magna-4 hot plate at setting 5. The Comparative Composite washeated until it was melted and then stirred for 2 minutes using astainless steel spatula. The resulting Comparative Composite melt wasremoved from the glass vessel using the spatula and placed on analuminum plate and allowed to cool to room temperature (23° C.), givinga solid plaque. All mixing, melting and cooling steps occurred inambient air.

Films were produced from a small portion of the Comparative Compositeplaque using a Carver Press preheated to 210° C. A sandwich was made byplacing an aliquot from the Comparative Composite plaque between twopolyimide polymer sheets. This sandwich was placed on the Carver Pressplatens, followed by bringing the platens together, melting the aliquotfrom the Comparative Composite plaque, resulting in a film between thepolyimide sheets. The sandwich was removed from the Carver Press, andthe sandwich was quenched at room temperature (23° C.) between twoaluminum plates. The polyimide sheets were peeled away, leaving a freestanding Comparative Composite film. FIG. 1 is an optical micrographimage of the Comparative Composite film. It shows that the Hybrane P/Sis not miscible with linear polystyrene and would be consideredunsuitable in a linear PS matrix.

Comparative Example 2

Into a glass vessel was charged 1.80 grams of a linear,non-hyperbranched polystyrene (Aldrich, average molecular weight 45,000)and 0.20 grams of Cloisite 10A (a functionalized organoclay having oniumsurface groups). The vessel was then placed on a Magna-4 hot plate atsetting 5. The Comparative Example 2 mixture was heated until visuallymelted and then stirred for 2 minutes using a stainless steel spatula.The resulting melt was removed from the glass vessel using the spatula,placed on a preheated glass slide, then allowed to cool to roomtemperature (23° C.), giving a solid film composite on the glass slide,defined here as Sample A. All mixing, melting and cooling steps occurredin ambient air.

The XRD results shown below in TABLE I show the basal plane spacing forSample A at each of 0, 2, 8, 24 hours of annealing at 225° C. in vacuum.At 0 hour, an increase in basal plane spacing was observed to beconsistent with polymer intercalation into the clay. Annealing at 225°C. resulted in a decrease in basal plane spacing indicating thatexfoliation of the clay did not occur.

Inventive Example 1

Into a glass vessel was charged 1.80 grams of hyperbranched polystyreneand 0.20 grams of Cloisite 10A (Cloisite 10A is a functionalizedorganoclay having onium surface groups). The vessel was then placed on aMagna-4 hot plate at setting 5. The Inventive Example 1 mixture washeated until visually melted and then stirred for 2 minutes using astainless steel spatula. The resulting melt was removed from the glassvessel using the spatula, placed on a preheated glass slide, thenallowed to cool to room temperature (23° C.), giving a solid filmcomposite on the glass slide, defined here as Sample B. All mixing,melting and cooling steps occurred in ambient air.

The XRD results shown below in TABLE I show the basal plane spacing forSample B at each of 0, 2, 8, 24 hours of annealing at 225° C. in vacuum.At 0 hour, an increase in basal plane spacing was observed consistentwith polymer intercalation into the clay. Complete clay exfoliationoccurred within 8 hours of annealing based on the loss of a basal planediffraction peak in the XRD diffraction pattern.

Inventive Example 2

Into a glass vessel was charged 1.80 grams of a linear,non-hyperbranched polystyrene (Aldrich, average molecular weight45,000), 0.16 g of hyperbranched polystyrene, and 0.04 grams of Cloisite10A (a functionalized organoclay having onium surface groups). Thevessel was then placed on a Magna-4 hot plate at setting 5. TheInventive Example 2 mixture was heated until visually melted and thenstirred for 2 minutes using a stainless steel spatula. The resultingmelt was removed from the glass vessel using the spatula, placed on apreheated glass slide, then allowed to cool to room temperature (23°C.), giving a solid film composite on the glass slide, defined here asSample C. All mixing, melting and cooling steps occurred in ambient air.

The XRD results shown below in TABLE I show the basal plane spacing forSample C at each of 0, 2, 8, 24 hours of annealing at 225° C. in vacuum.At 0 hour, an increase in basal plane spacing was observed consistentwith polymer intercalation into the clay. Complete clay exfoliationoccurred within 8 hours of annealing based on the loss of a basal planediffraction peak in the XRD diffraction pattern.

TABLE I Basal plane d-spacing (angstroms) after annealing at 225° C.Sample 0 hour 2 hours 4 hours 8 hours 24 hours A 38.4 15.7 14.8 14.814.8 B 42.1 42.1 Nearly Exfoliated Exfoliated Exfoliated C 36.7 36.7Nearly Exfoliated Exfoliated Exfoliated Neat 19.4 Cloisite 10AThe data in TABLE I show that Sample A containing linear,non-hyperbranched polystyrene does not exfoliate the clay while SamplesB and C that contained hyperbranched polystyrene, exfoliated the clay.

Typical Preparation of a Hyperbranched Polymer:

This synthesis is based on a method that has been described in Polymer2000, 41, 6027-6031 by Sherrington et al. A solution of 9.89 g (94.96mmoles) of styrene, 0.94 g (4.75 mmoles) of ethylene glycoldimethacrylate, 1.15 g of dodecanethiol, and 0.16 g (1.00 mmoles) of2,2′-azobisisobutyronitrile (AIBN) in 27 ml of toluene was sparged for10 minutes with nitrogen. The reaction mixture was then heated to 70° C.for 15 hours. The resulting polymer was precipitated into cold methanoltwice and dried in a vacuum oven at 60° C.

The invention has been described with reference to various embodiments.However, it will be appreciated that variations and modifications can beeffected by a person of ordinary skill in the art without departing fromthe scope of the invention.

1. An article comprising a matrix and a polymeric nanocompositecomprising a non-polar hyperbranched polystyrene resin and havingdispersed therein an exfoliated or intercalated onium functionalizedclay.
 2. The article of claim 1 that is in the form of a sheet or panel.3. The article of claim 1 that has been shaped by a molding processing.4. The article of claim 1 wherein the weight ratio of said matrix tosaid polymeric nanocomposite is from about 10:1 to about 100:1.
 5. Thearticle of claim 1 wherein said matrix is a polymeric matrix.
 6. Thearticle of claim 1 wherein said polymeric nanocomposite is substantiallyexfoliated.
 7. The article of claim 1 wherein said polymericnanocomposite comprises a smectite clay.
 8. The article of claim 1wherein said hyperbranched polystyrene has a molecular weight of fromabout 2,000 to about 1,000,000.
 9. The article of claim 1 wherein theweight ratio of said onium functionalized clay to said hyperbranchedpolystyrene is from about 1:1 to about 0.1:1.
 10. The article of claim 1wherein said hyperbranched polystyrene resin has from 95% to 100% of itsrecurring units that are derived unsubstituted styrene.
 11. The articleof claim 1 wherein said clay is a montmorillonite, hectorite, saponite,nontronite, beidellite, volhonskoite, sauconite, magadiite, medmontite,kenyaite, or vermiculite.
 12. The article of claim 1 wherein the clayhas been pretreated with an onium salt.